Effect of simulated rainfall and weathering on release of preservative elements from CCA treated wood

The release of arsenic from wood pressure-treated with chromated copper arsenate (CCA) can be decreased by application of wood finishes, but little is known about the types of finishes that are best suited for this purpose. This study evaluated the effects of finish water repellent content and ultraviolet (UV) radiation on the release of arsenic, copper, and chromium from CCA-treated wood exposed to simulated rainfall. Deck boards treated with CCA were either left unfinished or dipped in a finish prepared with 1%, 3%, or 5% water repellent. All specimens were exposed to leaching from simulated rainfall, and a subset of specimens was also exposed to UV radiation. The rainfall was collected and analyzed for total elemental arsenic, copper, and chromium. The water repellent significantly decreased the amounts of these elements in the runoff, but for the short duration of this study there was no difference among the three water repellent concentrations. It is possible that water repellent content would have a greater effect over a longer exposure period. Exposure to UV radiation caused a significant increase in leaching from both finished and unfinished specimens. This effect may be a result of increased surface area during weathering as well as loss of fibers caused by UV-induced surface erosion. 2003 This article is in PDF format (file size: 321 kb). To download this article, right click on the link immediately below and choose "save target as". To view the article, left click the link immediately below.
(Download the latest Acrobat Reader if required.)

Effect of simulated rainfall and weathering on release of preservative elements from CCA treated wood   (2003)

The release of arsenic from wood pressure-treated with chromated copper arsenate (CCA) can be decreased by application of wood finishes, but little is known about the types of finishes that are best suited for this purpose. This study evaluated the effects of finish water repellent content and ultraviolet (UV) radiation on the release of arsenic, copper, and chromium from CCA-treated wood exposed to simulated rainfall. Deck boards treated with CCA were either left unfinished or dipped in a finish prepared with 1%, 3%, or 5% water repellent. All specimens were exposed to leaching from simulated rainfall, and a subset of specimens was also exposed to UV radiation. The rainfall was collected and analyzed for total elemental arsenic, copper, and chromium. The water repellent significantly decreased the amounts of these elements in the runoff, but for the short duration of this study there was no difference among the three water repellent concentrations. It is possible that water repellent content would have a greater effect over a longer exposure period. Exposure to UV radiation caused a significant increase in leaching from both finished and unfinished specimens. This effect may be a result of increased surface area during weathering as well as loss of fibers caused by UV-induced surface erosion.

Author: Lebow, Stan; Williams, R. Sam; Lebow, Patricia

Source: Environmental science & technology. Vol. 37, no. 18 (2003): Pages 4077-4082.

Citation: Lebow, Stan; Williams, R. Sam; Lebow, Patricia  2003.  Effect of simulated rainfall and weathering on release of preservative elements from CCA treated wood  Environmental science & technology. Vol. 37, no. 18 (2003): Pages 4077-4082..